在蒸壓養護后會因為水料比的原因出現裂紋問題，導致在蒸壓養護后出現裂紋的還有其他方面的原因，只有它的安全性得到保障才能更好的為廣大用戶做好服務，也為廠家帶來更寬闊的市場。
　　
蒸壓澆注溫度過高：容易引起成型后期坯體產生裂紋，這類裂紋主要發生在模具中部熱量集中的部位；
Autoclaved pouring temperature is too high: the latter body prone to cracks forming such cracks occurred in the middle of the heat concentrated mold parts;　　
蒸壓配合比中：常由于石灰等鈣質材料使用過多而引起坯體總的發熱量過大、坯體過早失去流動性，從而造成裂紋，這類裂紋基本類似于水料比過小和澆注溫度過高造成的裂紋；
Mix in autoclaved: often due to excessive use of lime and other calcareous materials caused by excessive total body heat, body premature loss of mobility, resulting in cracks, crack such basic material similar to water ratio is too small and cracks caused by the pouring temperature is too high;
坯體的停放環境也是造成坯體裂紋的一大因素：其原因主要為環境溫度和濕度過低，使坯體周圍因溫度差或快速失水造成裂紋，這也是制品缺棱掉角的原因之一。
Body of the park environment is also a major cause body cracks factors: The main reason for the ambient temperature and humidity is too low, so that the temperature around the body due to dehydration caused by poor or rapid crack, which is product missing edge off angle reasons one.　　
還有與蒸壓養護沒有直接關系的，如負壓吊的吊運破壞，翻轉裂紋，發氣時憋氣裂紋等。都已在前面作了討論。值得提出的是，裂紋的反面就是粘連。因此，必須綜合考慮各種因素，從多方面入手，尋找合適的平衡點，實現生產質量目標。
There is no direct relationship with the autoclave curing, such as the destruction of vacuum lifting crane, flip crack, crack breath when fat gas. Have been discussed in front. It is noteworthy that the crack is the opposite of adhesions. Therefore, we must consider a variety of factors, from a multi-pronged approach, finding the right balance, production quality objectives.　　
當蒸壓養護操作不規范時解決方法：抽真空。及時放冷凝水。保證恒溫溫度和時間。